Note on Usage:
- Dry and clear the surface of work piece to pre prevent the porosity caused by moisture.
- For high carbon steel or alloy steel, preheat and interpass temperature is 150~250℃ to prevent the crack.
Chemical Composition & Hardness of All Weld Metal
 |
|
| Specimen specification and welding parameter | |
| Diameter (mm) | 2.8 |
| Current (A) | 300 |
| Voltage (V) | 32 |
| Interpass Temp (。C) | 150±15 |
| Shielding Gas | None |
| Polarization | DC(+) |
| Hardness of Weld Metal | |
| Layer | Hardness (HRC) |
| 1 | 8~10 |
| 2 | 10~12 |
| 3 | 10~14 |
| Work-Hardened | 45~50 |
| Chemical Composition of Weld Metal | |
| Chemical | unit: wt.% |
| C | 0.2 |
| Si | 0.5 |
| Mn | 15.7 |
| P | 0.035 |
| S | 0.021 |
| Cr | 12.31 |
| Available Sizes and Suggested Operating Range | |
| Size (mm) | 2.8 |
| Voltage （V） | 28~33 |
| Current（A） | 350~400 |
| ESO（mm） | 40~60 |
Microstructure of all weld metal
KCH-615-S produces an austenitic structure. Austenitic structure possesses high toughness and high work-hardening ability.
| This information is provided solely for the purpose of confirming product conformance with applicable standards. The serviceability of a product or structure utilizing this type of information is and must be the sole responsibility of the builder/user. Many variables beyond the control of JIE SHENG MACHINERY CO., LTD. affect the results obtained in applying this type of information. These variables include, but are not limited to, welding procedure, shielding gas, plate chemistry and temperature, weldment design, fabrication methods and service requirements. |